PAINTWORK

For your lacquer work, Dejond Metals is the right place. All aluminium pieces can be lacquered in the desired RAL colour at short notice. For this we work together with subcontractors. We only lacquer material bought at Dejond Metals. All goods are degreased, either manually or with vapour degreasing. Then the goods are roughened by blasting or sanding. After all pre-treatments, the goods are ready to be painted. This can be done in both powder and wet paint. We also have a limited number of flat aluminium sheets in stock that are already painted white in RAL 9010 as standard. Anodised aluminium pieces can also be lacquered. You can request the technical data sheets of all paints.

Aluminum paints

For your coating work, you've come to the right place at Dejond. All aluminum pieces can be coated in the desired RAL color, and this can be done quickly. For this, we collaborate with subcontractors. We exclusively coat materials purchased from Dejond.

All goods are degreased, either manually or through pickling - rinsing (2 times) - semi-rinsing - passivating. Afterward, these goods are roughened through blasting or sanding. After all pre-treatments, the goods are ready for coating. This can be done using either powder coating or wet coating.

We also have a limited number of flat aluminum plates in stock that are already standard white coated in RAL 9010. Anodized aluminum pieces can also be coated.

Types of Coatings

Powder coating is paint in powder form that is electrostatically sprayed onto the workpieces and then cured at a temperature of approximately 190 degrees Celsius. Result: layer thickness of approximately 100 microns.

Advantages
  o Quick processing
  o Environmentally friendly (no solvents)
  o Impact and scratch resistance
Disadvantages
o Limited color choices
  o Not all materials can be treated with this method
  o Length limitations

Wet coating is paint in liquid form. It is atomized onto the workpiece using a spray gun and compressed air. It can then dry and cure at room temperature. Result: layer thickness of approximately 90 microns.

Advantages
  o Virtually unlimited color choices
  o Beautiful, sleek finish
  o Practically all materials can be treated with this method

Disadvantages:
o More cumbersome process than powder coating
o Less impact-resistant